303 1.4305 stainless steel
- Grade:
Click To Email Seller
Specification, Chemical & Mechanical Performance
We can produce 303 1.4305 Stainless Steel stainless steel round rods, 303 1.4305 Stainless Steel forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With Bozhong Group production experience, strict control 303 1.4305 Stainless Steel chemical composition and 303 1.4305 Stainless Steel mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.
Round bar steel: 1mm to 3500mm
Square-shape steel: 1mm to 4000mm
Plate steel:0.1mm to 4000mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Standards – Alloy 303
ASTM/ASME:UNS S30300
EURONORM:FeMi35Cr20Cu4Mo2
DIN:1.4305
General Properties
Alloy 303 is a non-magnetic, austenitic stainless steel that is not hardenable by heat treatment. It is the free machining modification of the basic 18% chromium / 8% nickel stainless steel. Alloy 303 was specially designed to exhibit improved machinability while maintaining good mechanical and corrosion resistant properties Due to the presence of sulfur in the steel composition, Alloy 303 is the most readily machineable austenitic stainless steel; however, the sulfur addition does lower Alloy 303’s corrosion resistance to below that of Alloy 304. Like other austenitic grades, Alloy 303 demonstrates excellent toughness, although the sulfur does reduce this a little as well.
Applications
Alloy 303 is frequently used in applications that require parts to be heavily machined. Some examples include:
1、Nuts and bolts
2、Aircraft fittings
3、Gears
4、Screws
5、Shafts
6、Electrical switchgear components
7、Bushings
Corrosion Resistance
- Good resistance to mildly corrosive atmospheres, but significantly less than Alloy 304
- When additional sulfur is added to improve machinability, it can often slightly reduce corrosion resistance
- In most dry and mild corrosive environments, Alloy 303 is comparable to other unmodified alloys
- Should not be exposed to moist, marine environments as it is subject to rapid-pitting corrosion and a rust film will tend to form
- Like other common austenitic stainless steels, it is subject to corrosion cracking in chloride environments above 60oC
Heat Resistance
- Good oxidation resistance at temperatures up to 1700oF (927 oC)
- Continuous use at temperatures above 1400oF (760oC) is not usually recommended due to carbide precipitation which can lead to irregular scaling
- Does not have a low carbon content so it is also vulnerable to sensitisation
Chemical Properties:
% | Cr | Ni | C | Si | Mn | P | S | Mo | Fe |
---|---|---|---|---|---|---|---|---|---|
303 | min: 17.0 max:19.0 |
min: 8.0 max: 10.0 |
0.15 max |
1.00 max |
2.0 max |
0.20 max |
0.15 min |
0.75 | balance |
Mechanical Properties:
Grade | Tensile Strength ksi (min.) | Yield Strength 0.2% Offset ksi (min.) | Elongation - % in 50 mm (min.) | Hardness (Brinell) MAX | Hardness (Rockwell B) MAX |
---|---|---|---|---|---|
303 | 75 | 30 | 35 | 228 |